Polycrystalline Mullite Fiber Boards for Kiln Insulation 1700c/1800c/1900c

• Customization: Available
• Shape: Ceramic Fiber Plate
• Manufacturing Technique: Vacuum Shaped
• Model NO.: NR1700, NR1800
• Kind: High Ahlmirla Fibre
• Temperature Grade: 1700c-1800c-1900c
• Standard Size: 1000X600X 25-50mm
• Density: 350-700 Kg/M3
• Delivery Time: Usually for Regular Order Within 14 Days
• Transport Package: by PP Bags, Carton and Then by Pallet
• Specification: ISO9001
• Trademark: NR
• Origin: China
• HS Code: 68061010
• Production Capacity: 5000 PCS/Mo

Product Description

Find 1600ºC,1700ºC ,1800ºC,1900ºC Ceramic Board [polycrystal] for Your Kilns,furnaces

NR® high-density ultra high temperature ceramic fiber board products are available in formulations for service temperatures up to 1800°C.  NR® high-density boards are available for high temperature, oxidizing environments  and high temperature, reducing environments . NR® boards are formed from alumina or mullite polycrystalline fibers with appropriate inorganic and organic binders. All grades are pre-fired to 1000°C or greater, resulting in an organic free composition. Possible applications include furnace hearth plates and low mass sintering setters.

Features

• High temperature stability, good performance against heat shock and erosion.
• Low heat capacitance, low thermal conductivity.
• Hard and high internal adhesive strength allow it with good performance for machining and cutting.
• Can have direct contact with flame, easy for installation and use.

Application scope:

• Ceramic industry: kiln liner, kiln car
• Glass industry
• Piping heat insulation, common heat resisting material
• Other high temperature insulation

Item		Specification	Testing Result
Max Service Temp  C		1600	1600
Continous Service Temp C		1500	1500
Density     kg/m3		≥380	400
Hardness		≥50	70
Rupture Strength         MPa		_	0.6
Linear Change     %	1500C×8hr	≤2	0.1
Thermal Conductivity    w/mk	at 600C	_	0.14
	at 800C	_	0.17
	at 1000C	_	0.24
Chemical      %	Al2O3	≥60	64
	Al2O3+SiO2	≥97	98
the above is typical testing result
Item		Specification	Testing Result
Max Service Temp  C		1700	1700
Continous Service Temp C		1600	1600
Density     kg/m3		≥330	350
Hardness		≥50	72
Rupture Strength         MPa		_	0.7
Linear Change     %	1600C×8hr	≤2	0.2
Thermal Conductivity    w/mk	at 600C	_	0.15
	at 800C	_	0.19
	at 1000C	_	0.25
Chemical      %	Al2O3	≥63	75
	Al2O3+SiO2	≥97	99
Item		Specification	Testing Result
Max Service Temp  C		1800	1800
Continous Service Temp C		1700	1700
Density     kg/m3		≥380	400
Hardness		≥50	78
Rupture Strength         MPa		_	1.0
Linear Change     %	1700C×8hr	≤2	0.1
Thermal Conductivity    w/mk	at 600C	_	0.20
	at 800C	_	0.23
	at 1000C	_	0.29
Chemical      %	Al2O3	≥69	75
	Al2O3+SiO2	≥98	99